PDF全文下载：2017020095
周梦飞1， 王永雷1， 牛强1， 韩伯群2， 赵程1*
(1.青岛科技大学 机电工程学院，山东 青岛266061; 2.江苏丰东热技术有限公司，江苏 大丰224100)
摘要：利用直流等离子体辉光放电技术对双相不锈钢表面进行了低温离子渗碳硬化处理，主要研究了渗碳温度和渗碳时间对硬化层的影响。利用显微硬度计测试了渗碳层的表面硬度和硬度梯度；用光学显微镜观察了渗碳层横截面金相组织；用X-射线衍射仪分析了渗碳层的结构。分析结果表明：双相不锈钢表面渗碳层的硬度和厚度都随着渗碳温度的提高和渗碳时间的延长而提高，并且开始时增长速度比较快，超过某一值后变化趋于平缓。在430~490℃范围内，双相不锈钢表面可以实现在不降低耐蚀性能的前提下，得到高硬度及高厚度的硬化层。
关键词：双相不锈钢；低温离子硬化；离子渗碳；耐蚀性
中图分类号：TG 156.8文献标志码：A
引用格式：周梦飞，王永雷，牛强，等.双相不锈钢表面低温离子渗碳硬化处理［J］.青岛科技大学学报(自然科学版), 2017, 38(2): 95-99.
ZHOU Mengfei，WANG Yonglei，NIU Qiang，et al.Plasma carburizing hardening treatment of duplex stainless steel at low temperature［J］. Journal of Qingdao University of Science and Technology（Natural Science Edition), 2017, 38(2): 95-99.
Plasma Carburizing Hardening Treatment of Duplex Stainless Steel at Low Temperature
ZHOU Mengfei1， WANG Yonglei1， NIU Qiang1， HAN Boqun2， ZHAO Cheng1
(1.College of Electromechanical Engineering,Qingdao University of Science and Technology, Qingdao 266061,China;2.Jiangsu Fengdong Heat Treatment Co.,Ltd.,Jiangsu 224100, China)
Abstract: Surface hardening of duplex stainless steel was carried out using plasma carburizing process at low temperature, mainly studied the influence of carburized temperature and time on the properties of hardening layer. The surface hardness, hardness gradient, surface brittleness of the carburized layer was tested by Vickers hardness tester. The cross-section′s microstructure of the carburized layer was observed by optical microscope. The phase structure of the carburized layer was measured by X-ray diffraction analysis. The results showed that the surface hardness and harden layer thickness increased with the raising of the treatment temperature and time. At the beginning, the growth rate is relatively fast, but when it is more than a certain value, the changes will be flatten. In the temperature range of 430—490 ℃, the surface of duplex stainless steel can get a harden layer of high hardness and high thickness without reducing the corrosion resistance.
Key words: duplex stainless steel; plasma hardening at low temperature; plasma carburizing; corrosion resistance
收稿日期：2015-11-04
作者简介：周梦飞（1990—），男，硕士研究生.*通信联系人.
文章编号：1672-6987（2017）02-0095-05；DOI：10.16351/j.1672-6987.2017.02.015